ZDS-CA1829 Shaft Wear Repair Compound
ZDS-CA1829 repairs and rebuilds worn areas on shafts, pumps and machine surfaces. Its ceramic-filled compound supports dimensional restoration and wear resistance.
Product overview
Shaft Wear Repair Compound
ZDS-CA1829 is a paste compound for repairing and rebuilding worn areas on pumps, shafts, bearing seats, machine surfaces and industrial pipelines. It helps restore the dimensions of a damaged area during maintenance.
Its ceramic-filled composition provides a wear-resistant material option for severe-service repair areas. The practical fit depends on the repair size, required finished shape and access to the component.
Key material properties
- Dimensional restoration: For rebuilding worn areas toward the required component dimensions.
- Wear resistance: A useful property when selecting material for worn industrial surfaces.
- Ceramic-filled material: A protective material option for the equipment and exposure described for this product.
Evaluate the material
ZDS-CA1829 technical specifications
| Property | Value / conditions |
|---|---|
| Product model | ZDS-CA1829 |
| Product series | ZDS-CeramicArmor |
| Product family | Wear & erosion protection |
| Substrates and equipment | Pumps and pump casings, shafts, bearing seats and machine surfaces, industrial pipelines |
| Form and color | Paste; Typical: Dark grey |
| Working time at 25°C | Typical: 30-45 min |
| Initial cure at 25°C | Typical: 4-6 h |
| Full cure / cure conditions | 24 h |
| Service temperature | -60 to 180°C |
| Recommended application temperature | Recommended: 10°C to 35°C |
| Recommended application thickness | Recommended: 3-10 mm |
Questions about your operating conditions?
Repair and Rebuilding Applications
Worn pump and machine surfaces
ZDS-CA1829 is used to rebuild worn areas on pumps, pump casings, shafts, bearing seats and other machine surfaces. Its dimensional restoration property helps bring a damaged area toward the required component shape during repair.
Repairs where wear is a key concern
The ceramic-filled compound suits repair areas exposed to severe service where wear resistance matters. Choose it by checking the damaged dimensions, the finished shape needed and the access available around the component.
Prepare the work surface
Prepare the repair area using the product-specific preparation instructions.
- Inspect the damaged area and the surrounding component for loose material and contamination.
- Arrange access to the full work area and the tools needed for the next step.
- Address contamination using the preparation method specified for this product and the actual surface.
Plan the work
Application and cure planning
- Prepare the repair area and arrange access and tools before starting.
- Mix the components according to the product instructions after surface preparation and setup are complete.
- Place and shape the repair material according to the product instructions.
- Use the technical table to plan the cure stages. Follow the applicable repair or application procedure for handling, loading and return to service.
Product selection questions
How much working time is available?
The typical working time at 25°C is 30-45 min. Complete surface preparation and setup before mixing.
What is the full-cure schedule?
Full cure: 24 h. Follow the product instructions for the applicable cure conditions.
What temperatures apply?
Recommended application temperature: 10°C to 35°C. Service temperature: -60 to 180°C. Application and service temperatures describe different conditions.
What thickness is recommended?
Recommended: 3-10 mm. Use the stated thickness type and range when planning the work.